Tailoring the refractive index of impedance

Scientific Reports volume 12, Article number: 15818 (2022) Cite this article

746 Accesses

Metrics details

Independent control of the magnetic and electric properties of two-part and three-part ferrite composites is demonstrated through variation of particle size and volume fraction of ferrite inclusions. This provides a route to creating broadband impedance-matched composites with tailored high refractive-index values. A two-part composite comprising NiZn ferrite in a PTFE dielectric host with approximately equal values of relative real permittivity and permeability up to 100 MHz is manufactured. The refractive index for NiZn–PTFE composites, measured at 20 MHz, is 6.1 for NiZn volume fraction of 50%vol. and 6.9 for NiZn volume fraction of 70%vol. Similarly, we have characterised a three-part composite with a refractive index of approximately 16 up to 60 MHz. The three-part composite comprises NiZn and MnZn ferrites in a PTFE dielectric host matrix with a percentage volume ratio of 65%: 15%: 20%, respectively.

Commercially available soft ferrites have been used extensively in telecommunications and antenna systems due to their simultaneously high real part of permeability, and low magnetic loss in the MHz frequency range1. The high real part of permeability not only increases the refractive index for composite materials, aiding miniaturisation, but also increases the characteristic impedance towards the impedance matched case of Z \(=1.\) It is well known that the frequency dependence of the permeability diminishes at higher (GHz) frequencies due to domain wall relaxation and gyromagnetic relaxation: a phenomenon that is described by Snoek’s law2. Since Snoek’s original article appeared in 1948, there have been many studies extending this concept to apply to thin magnetic films and composite materials3,4,5. The original law does not account for the size or the shape of the magnetic particles if the ferrite is powdered and mixed with a host material. The size and shape of the particles and the filling fraction of the resulting composite offer additional freedoms to tune the frequency dependence of the magnetic response. For example, the shape anisotropy of magnetic inclusions can be increased by using magnetic flakes, increasing the frequency at which a strong magnetic response can be observed6,7. Materials with a planar crystalline geometry, such as M-type hexafarrites, have increased magnetocrystalline anisotropy, extending the frequency range of magnetic performance8.Of course, these same degrees of freedom also influence the dielectric (permittivity) response of the composite. In this study we demonstrate that the relative permittivity (\(\varepsilon = \varepsilon^{\prime} - i\varepsilon^{\prime\prime}\)) and permeability (\(\mu = \mu^{\prime} - i\mu^{\prime\prime}\)) of the composite are influenced by the particle size of ferrite inclusions. If the properties of the magnetic particles in composites are carefully controlled, high refractive index (\(n=\sqrt{\varepsilon \mu }\)) materials that are impedance matched (\(Z=\sqrt{\mu /\varepsilon }\)) to free space can be manufactured. These materials with high refractive index and impedance matching to free space are important for the miniaturisation of antennas.

NiZn and MnZn ferrites are magnetically ‘soft’ due to their low magnetic coercivity, meaning they do not retain magnetism after being subject to a magnetic bias. The general chemical formula for spinel ferrites is MFe2O4, where ‘M’ is a divalent metal. The spinel crystal structure, with a cubic close-packed arrangement of metallic ions surrounded by oxygen ions, leads to a high magnetocrystalline anisotropy due to the ordering of electron spins9. Studies of the effect of ferrite particle size and percentage volume loading of composites on the resulting complex permeability of a dielectric-based composite are not new. For example, Dosoudil et al.10 fabricated three sets of composite samples, using commercially available MnZn and NiZn ferrite powdered ceramics in a polyvinyl chloride (PVC) matrix. In their paper, they explore the effect of particle size on the permeability, fixing the volume loading (65% vol.) of the ferrite powder and MnZn:NiZn ratio (80%: 20%). A typical Snoek’s Law dependence was observed, characterised by a resonant peak in the imaginary component of the permeability, which shifts to higher frequencies with increasing particle size. The real part of the relative permeability (\(\mu^{\prime }\)) at 20 MHz increased from approximately 16 (for < 40 µm sized particles) to approximately 20 (for 80–250 µm sized particle). The increase in permeability with increasing particle size is associated with the increase in number of magnetic domains within the ferrite particles, and will be discussed later.

Slama et al.11 investigated the coercivity and low frequency permeability (at 100 kHz) as a function of grain size for a bulk-sintered NiZn ferrite. A linear relationship between the low frequency permeability and the grain size (for a grain size range of 2–15 µm) was observed, while an inverse relationship was found between the coercivity and the grain size. These results indicate that the intrinsic magnetic properties are significantly affected by the microstructure of the ferrite and this will be discussed later in this paper.

Of course, it is not just the magnetic properties that are affected by the ferrite particle size in composites, the dielectric properties are also altered. The effect of particle size on both the real permeability and permittivity of hexagonal ferrites has been investigated by Li et al.12. In that study the particle size of a 70% vol. hexagonal ferrite composite (\({\mathrm{Ba}}_{3}{\mathrm{Co}}_{2}{\mathrm{Fe}}_{24}{\mathrm{O}}_{41}\)) in a polyvinylidene fluoride polymer matrix was varied over the three particle size ranges; 75–150, 38–50 and 10–30 µm. At 20 MHz, the real part of the relative permeability increased from 3 to 4.8 for ferrite particle size ranges 10–30 µm and 75–150 µm, respectively, while the corresponding relative real permittivity also increased from 50 to 75. Parsons et al. also investigated how particle size affects the permeability and permittivity of polycrystalline NiZn ferrite nanoparticles in polymer composites13. In their study, co-precipitated NiZn nanoparticles were used to create a near impedance matched material with permittivity and permeability approximately equal to 4.5 across the frequency range 300–500 MHz. Li et al. performed studies into the particle size effects for composites comprising Co-Ti substituted M-type hexaferrite composites14, and presented a modified effective medium theory to predict the magnetodielectric properties. The modified effective medium theory shows magnetic permeability to have a strong dependence on particle size, particularly when the distribution of particle size is narrow.Li et al. also investigated the importance of magnetocrystalline anisotropy for M-type hexaferrites when prepared by one-step or two- step sintering procedures. By preparing hexaferrites by a two-step sintering procedure, a fine grained microstructure can be achieved with uniform domains. The uniform domains have enhanced high-frequency permeability with minimised loss. Composite samples with 89% density Co-Ti substituted barium hexaferrite in polyvinyl alcohol had a real part of permeability of 15, extending up to 500 MHz. The relative permittivity was significantly lower, at 10.8.

In this present study, the commercially available sintered NiZn-ferrite powder and sintered MnZn-ferrite, supplied by MagDev Ltd (UK), were used to produce cold-compressed NiZn-ferrite–PTFE and NiZn-MnZn-ferrite–PTFE composites. X-ray diffraction measurement confirmed the phase compositions of NiZn ferrite to be \({\mathrm{Ni}}_{0.4}{\mathrm{Zn}}_{0.6}{\mathrm{Fe}}_{2}{\mathrm{O}}_{4}\) (with minor impurity phases of \(\mathrm{NiO}\), \(\mathrm{ZnO}\), \({\mathrm{Fe}}_{2}{\mathrm{O}}_{3}\) and \({\mathrm{Fe}}_{3}{\mathrm{O}}_{4})\) and MnZn ferrite to be \({\mathrm{Mn}}_{0.8}{\mathrm{Zn}}_{0.2}{\mathrm{Fe}}_{2}{\mathrm{O}}_{4}\) (with minor impurity phases of \({\mathrm{Fe}}_{3}{\mathrm{O}}_{4}\), \({\mathrm{Fe}}_{2}{\mathrm{O}}_{3}\) and MnO). The presence of impurity phases means ferrous and ferric ions exist within the bulk of the grains. These ferrous and ferric ions facilitate electron hopping across crystal sites in the grains, thus reducing the resistivity of the material and increasing the permittivity15.

Laser-diffraction measurements were taken using a Mastersizer2000 supplied by Malvern Instruments Ltd. (UK) gave the modal particle diameter for the NiZn ferrite powder as 4 µm. While the modal value for the particle size was below 10 µm, the range of particle sizes was between 1 and 200 µm. The values of the real part of its static relative permeability and relative permittivity as specified by MagDev Ltd. are 125 and 100. The particle size for the powder was separated into different size ranges using a vibrating sieve to produce eight size ranges: 125–90 µm; 90–75 µm; 75–63 µm; 63–53 µm; 53–45 µm; 45–38 µm; 38–20 µm and < 20 µm. The average particle size and uncertainty for each sieved fraction was measured via laser diffraction, and the size distribution deduced was found to be in good agreement with the size of the corresponding sieve-mesh.

To characterise the electromagnetic properties, composites were fabricated using each sieved sample. The NiZn ferrite powder fraction was mixed with powdered PTFE with mean particle diameter of 35 µm according to supplier, Sigma Aldrich Ltd. The powders were mixed by simply stirring the powders in a metal cylinder before sealing and shaking the mixture by hand. The powder mix was poured into a cylindrical, hardened steel mould that had been sprayed with silicone mould-release spray. The mix was then pressed in the mould under 55 MPa for 300 s to produce millable composite samples with a diameter of 30 mm and height between 5 and 10 mm. Samples were made with volume fractions of 15, 30, 50 and 70% NiZn ferrite powder (32 individual samples in total).

Similarly, a three-part composite containing 15% vol. MnZn ferrite, 65% vol. NiZn ferrite and 20% vol. PTFE was fabricated via the same method. The NiZn ferrite was used with the as-provided particle size distribution mentioned above, without any sieving. Laser diffraction measurements revealed that the MnZn ferrite powder had a median particle diameter of 35 µm, and the static values of real part of the permeability and permittivity as specified by MagDev are \({10}^{3}\) and \({10}^{5}\) respectively.

The samples were electromagnetically characterised using the stripline technique developed by Barry16. The stripline geometry had a signal line width, w = 19.40 mm, a signal line thickness, t = 0.10 mm, and a groundplane separation, h = 13.40 mm, indicated in Fig. 1. The signal line had a standard 20O taper from coaxial pin to final strip width. Each of the samples were milled into two identical cuboid shapes with each of the sample pairs placed above and below the signal line to fill the transmission line cross-section. The cuboid shapes had a 0.05 mm deep slot with width 19.40 mm milled to accommodate the conducting strip of the transmission line. The stripline was connected to a Vector Network Analyser (VNA) that was calibrated using ‘Short’, ‘Open’, ‘Load’ and ‘Through’ standard calibration (SOLT calibration) to set the reflection planes to the ends of coaxial cables. The complex reflection and transmission coefficients of the samples was measured by inserting the ferrite samples into the stripline and measuring the complex S11 and S21 parameters. From these complex S-parameters together with the frequency and the thickness of the sample, the relative complex permittivity and permeability are both obtained using the Nicholson, Ross, Weir (NRW) extraction method17,18.

Cross-section schematic for the stripline geometry, showing width of central conductor, w, thickness of central conductor, t, and height of stripline cavity, h.

Figure 2 shows the real parts of the relative permittivity and permeability at 20 MHz as a function of the average NiZn ferrite particle size for a NiZn ferrite-PTFE composite for (a) 15% vol., (b) 30% vol., (c) 50% vol. and (d) 70% vol. All four plots show that both the permeability and permittivity increase as a function of the NiZn ferrite particle size; however, the permeability is more strongly dependent on the particle size in comparison to the permittivity. For example, in Fig. 2d, the permittivity increases from 7.0 (for an average particle size of 4.2 µm) to 7.9 (for an average particle size of 147 µm) while the corresponding permeability value increases from 5.5 to 12.5 for the same particle size increase. The increase in permeability with increased particle size can be understood by considering the distribution of the demagnetising fields for particles containing differing numbers of domains.

Plots of the relative real permittivity (εˊ) and permeability (μˊ) at 20 MHz as a function of the average NiZn ferrite particle size for a NiZn ferrite-PTFE composite with (a) 15% vol., (b) 30% vol., (c) 50% vol. and (d) 70% vol. loading of ferrite material. The average particle size and uncertainty were deduced from laser diffraction measurements.

Studies into the domain structure of MnZn ferrite have found that mono-domains exist in grains that are approximately 4 µm or less in size19. The domain structure and number of domains is dictated by the internal energy of the particle with the magnetostatic energy and the exchange energy competing. The magnetostatic energy is minimised by division of the particle into more domains, reducing domain size, while the exchange energy is minimised by aligning adjacent spins, increasing domain size. As the particle subdivides into more domains, the coercivity decreases as less magnetic force is required to move domain walls than to rotate the magnetisation vectors of entire domains. In general, magnetic materials with a low coercivity value possess a large permeability20 as they can be magnetised more easily.

Figure 2 also shows a weak dependence of the permittivity on particle size. This can be understood by considering the grain structure within each of the ferrite particles. The dielectric properties of ferrites originate from their granular structure, being composed of semi-conducting grains. An electron hopping process takes place across crystal lattice sites within the grains that have ferric and ferrous ions15. In grain boundaries, impurity ions replace the ferrous ions and suppress the hopping effect, increasing resistivity21. A capacitive effect between internal barrier layers (IBLC) can be manifest in Mn–Zn ferrites, leading to a ‘giant dielectric phenomenon’22,23. It has been documented that the presence of the grain boundaries greatly increases the relative permittivity of the ferrite, as capacitive effects arising from the separation of the charges enhance the permittivity24. The larger ferrite particles in this study are composed of more grains and insulating grain boundaries compared to smaller ferrite particles. In some cases, very small particles less than 10 µm can be mono-grain25. Therefore, the permittivity of the smaller ferrite particles is reduced since the capacitive effects arising from the grain boundaries, are reduced.

Figure 2 demonstrates that for the more heavily loaded composites, 50–70% vol., equal values of the real parts of the relative permittivity and permeability can be obtained by tuning the ferrite-particle size between 25 and30 μm. The corresponding refractive index values of the composites are 6.1 (50% vol.) and 6.9 (70% vol.) respectively at 20 MHz. If the ferrite composite has low electromagnetic loss, this offers the exciting prospect of a high-index, impedance matched material.

Figure 3 shows the complex relative permeability as a function of frequency for eight 70% vol. NiZn ferrite-PTFE composites containing different particle size ranges, showing (a) the real part, and (b) the imaginary part of the relative permeability. These plots show that the change in the frequency dispersion of the complex permeability for composites containing different particle sizes follows Snoek’s Law2. That is, the relative permeability falls off faster with frequency when the initial value for the real part is higher. The frequency dispersion of the relative permeability behaves in a similar manner to that of the complex permeability for composites containing different volume fractions of ferrite filler where larger particles give a larger initial relative permeability, similar to a higher volume fraction of ferrite loading.

Plots of the complex relative permeability as a function of frequency for eight 70% vol. NiZn ferrite-PTFE composites containing different particle size ranges: (a) the real part of the relative permeability, while (b) the imaginary permeability.

In the final part of this study, a three-part composite containing MnZn ferrite, NiZn ferrite and PTFE is fabricated as an alternative approach to engineering impedance matched, high-index materials. The proportions of each component were chosen to provide the highest possible refractive index of the composite under the assumption that samples can be fabricated with a maximum ferrite loading volume fraction of 80% vol. PTFE powder was used as the dielectric matrix. Figure 4a shows the frequency dependent complex permittivity and permeability for a composite containing 65% vol. NiZn ferrite (modal particle size 4 µm), 15% vol. MnZn ferrite (modal particle size 35 µm) and 20% vol. PTFE (particle size < 35 µm). For this part of the study, the powders are used in the as-received state directly from the manufacturer. That is, the particles sizes for the ferrite inclusions did not undergo any secondary sieving stage. The real parts of the permittivity and permeability are closely matched below 100 MHz, with the relative impedance falling to 94% of its low-frequency value at 100 MHz (Fig. 4b). The measured transmissivity is near complete (> 98%) with the refractive index at n ~ 16. With a higher index dielectric host material, higher values for refractive index may be obtained. The PTFE host material has a dielectric permittivity of around 2.2, corresponding to a refractive index of 1.4826. Above 100 MHz there is an increasing mismatch of complex permittivity and permeability associated with the domain wall relaxation27,28. At 4 GHz, the absorbance increases to 60% due to the increase in the imaginary part of permeability, while the relative impedance decreases to 0.28 due to the reduction of the real part of permeability.

(a) Plot of the complex relative permeability and permittivity as a function of frequency and (b) reflected and transmitted intensity, absorption and the relative impedance as a function of frequency for a 65% vol. NiZn ferrite, 15% vol. MnZn ferrite and 20% vol. PTFE composite.

In conclusion, both the relative real permeability and permittivity for NiZn ferrite-PTFE composites were found to increase with increasing ferrite particle size. The permeability exhibited a far stronger particle size dependence in comparison to the permittivity, allowing an impedance matched condition to be met at 20 MHz for particle sizes of 25–30 µm with both 50 and 70% vol. NiZn ferrite composites. The corresponding refractive index values of these two composites are 6.1 and 6.9 respectively. A third component, MnZn ferrite, added to NiZn ferrite-PTFE composites allows the relative permittivity and permeability to both equal 16.1 from10 to 50 MHz. The ability to alter the permeability and permittivity by controlling the particle size in magnetic composites or introducing a third component allows for desired EM properties, such as broadband impedance matching to free space to be engineered. Components requiring high refractive index, low electromagnetic loss materials, such as lenses and miniaturised antennas will benefit from these composites.

The datasets generated and/or analysed during the current study are available in the University of Exeter repository, Open Repository Exeter (ORE), reference29 gives a web link for this repository.

Dionne, G. F. Magnetic Oxides (Springer, 2009).

Book Google Scholar

Snoek, J. Dispersion and absorption in magnetic ferrites at frequencies above one Mc/s. Physica 4, 207 (1948).

Article ADS Google Scholar

Chai, G., Xue, D., Fan, X., Li, X. & Guo, D. Extending the Snoek’s limit of single layer film in (Co96Zr4∕Cu)n multilayers. Appl. Phys. Lett. 93, 152516 (2008).

Article ADS Google Scholar

Acher, O. & Dubourg, S. Generalization of Snoek’s law to ferromagnetic films and composites. Phys. Rev. B 77, 104440 (2008).

Article ADS Google Scholar

Lagarkov, A. & Rozanov, K. High-frequency behavior of magnetic composites. J. Magn. Magn. Mater. 321, 2082 (2009).

Article ADS CAS Google Scholar

Shirakata, Y., Hidaka, N., Ishitsuka, M., Teramoto, A. & Ohmi, T. Low-loss composite material containing fine Zn–Ni–Fe flakes for high-frequency applications. IEEE Trans. Mag. 45, 4337 (2009).

Article ADS CAS Google Scholar

Wang, Y. & Grant, P. NiZn ferrite/Fe hybrid epoxy-based composites: Extending magnetic properties to high frequency. Appl. Phys. A 117, 477 (2014).

Article CAS Google Scholar

Li, Q., Chen, Y., Yu, C., Qian, K. & Harris, V. G. Permeability spectra of planar M-type barium hexaferrites with high Snoek’s product by two-step sintering. J. Am. Ceram. Soc. 103, 5076–5085 (2020).

Article CAS Google Scholar

Misra, S., Karan, T. & Ram, S. Dynamics of surface spins in small core-shell magnets of Li0.35Zn0.30Fe2.35O4 bonds over a carbon. J. Phys. Chem. C 119, 23184 (2015).

Article CAS Google Scholar

Dosoudil, R., Usakova, M., Franek, J., Slama, J. & Gruskova, A. Particle size and concentration effect on permeability and EM-wave absorption properties of hybrid ferrite polymer composites. IEEE Trans. Magn. 46, 436 (2010).

Article ADS CAS Google Scholar

Slama, J. et al. The influence of particle size and substituent contents on the magnetic properties of Be or Cu substituted NiZn ferrites. Adv. Electr. Electron. Eng. 5, 362 (2011).

Google Scholar

Li, B., Shen, Y., Yue, Z. & Nan, C. Influence of particle size on electromagnetic behavior and microwave absorption properties of Z-type Ba-ferrite/polymer composites. J. Magn. Magn. Mater. 313, 322 (2007).

Article ADS CAS Google Scholar

Parsons, P., Duncan, K., Giri, A. K., Xiao, J. Q. & Karna, S. P. Electromagnetic properties of NiZn ferrite nanoparticles and their polymer composites. J. Appl. Phys. 115, 173905 (2014).

Article ADS Google Scholar

Li, Q., Chen, Y. & Harris, V. G. Particle-size distribution modified effective medium theory and validation by magneto-dielectric Co-Ti substituted BaM ferrite composites. J. Magn. Magn. Mater. 453, 44–47 (2018).

Article ADS CAS Google Scholar

Birajdar, A. A. et al. Frequency and temperature dependent electrical properties of Ni0.7Zn0.3CrxFe2−xO4 (0 ≤ x ≤ 05). Ceram. Int. 38, 2963–2970 (2012).

Article Google Scholar

Barry, W. & Broad-Band, A. Automated, stripline technique for the simultaneous measurement of complex permittivity and permeability. IEEE Trans. Microw. Theory Technol. 34, 80 (1986).

Article ADS Google Scholar

Nicolson, A. & Ross, G. Measurement of the intrinsic properties of materials by time-domain techniques. IEEE Trans. Instrum. Meas. 19, 377 (1970).

Article Google Scholar

Weir, W. Automatic measurement of complex dielectric constant and permeability at microwave frequencies. Proc. IEEE 62, 33 (1974).

Article Google Scholar

Goldman, A. Modern Ferrite Technology 2nd edn. (Springer, 2010).

Google Scholar

Cullity, B. D. & Graham, C. D. Introduction to Magnetic Materials 2nd edn. (John Wiley & Sons, 2011).

Google Scholar

Jahan, N. et al. Correlation among the structural, electric and magnetic properties of Al3+ substituted Ni–Zn–Co ferrites. RSC Adv. 12, 15167 (2022).

Article CAS Google Scholar

Koops, C. On the dispersion of resistivity and dielectric constant of some semiconductors at audiofrequencies. Phys. Rev. 83, 121 (1951).

Article ADS CAS Google Scholar

Loyau, V. et al. An analysis of Mn-Zn ferrite microstructure by impedance spectroscopy, scanning transmission electron microscopy and energy dispersion spectrometry characterizations. J. App. Phys. 111, 053928 (2012).

Article ADS Google Scholar

Adams, T., Sinclair, D. & West, A. Giant barrier layer capacitance effects in CaCu3Ti4O12 ceramics. Adv. Mater. 14, 1321 (2002).

3.0.CO;2-P" data-track-action="article reference" href="https://doi.org/10.1002%2F1521-4095%2820020916%2914%3A18%3C1321%3A%3AAID-ADMA1321%3E3.0.CO%3B2-P" aria-label="Article reference 24" data-doi="10.1002/1521-4095(20020916)14:183.0.CO;2-P">Article CAS Google Scholar

Kawano, K., Hachiya, M., Iijima, Y., Sato, N. & Mizuno, Y. The grain size effect on the magnetic properties in NiZn ferrite and the quality factor of the inductor. J. Magn. Magn. Mater. 321, 2488 (2009).

Article ADS CAS Google Scholar

Qiang, W. Y., Yong, W., Bin, L., Ye, Z., Ping, D. G. Application in measuring the microwave complex permittivity of cylindrical dielectric by using a terminal loaded coaxial probe. In ICEMI 4–46 (2007).

Tsutaoka, T. Frequency dispersion of complex permeability in Mn–Zn and Ni–Zn spinel ferrites and their composite materials. J. Appl. Phys. 93, 2789 (2003).

Article ADS CAS Google Scholar

Beatrice, C. et al. Magnetic losses versus sintering treatment in Mn-Zn ferrites. J. Magn. Magn. Mater. 429, 129–137 (2017).

Article ADS CAS Google Scholar

Parke, L et al. Tailoring the Refractive Index of Impedance-matched Ferrite Composites. http://hdl.handle.net/10871/130799 (University of Exeter ORE).

Download references

The authors wish to acknowledge the financial support of the EPSRC and DSTL for funding LP’s PhD studentship through the University of Exeter Doctorial Training account, and JRS, IJY, and APH acknowledge support by EPSRC through the QUEST programme grant (EP/I034548/1) “The Quest for Ultimate Electromagnetics using Spatial Transformations.”

Electromagnetic and Acoustic Materials Group, Department of Physics and Astronomy, University of Exeter, Stocker Road, Exeter, EX4 4QL, UK

L. Parke, C. P. Gallagher, A. P. Hibbins & J. R. Sambles

Defence, Science and Technology Laboratory, Salisbury, SP4 0JQ, UK

I. J. Youngs

You can also search for this author in PubMed Google Scholar

Author 1, L.P., collected the data under the supervision on Authors 2, 4 and 5 (I.Y., A.H. and R.S.). The figures and manuscript were initialised by Author 1, L.P. and edited by Author 3 and 5 (C.G. and R.S.) before submission. All authors reviewed the manuscript.

Correspondence to C. P. Gallagher.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Parke, L., Youngs, I.J., Gallagher, C.P. et al. Tailoring the refractive index of impedance-matched ferrite composites. Sci Rep 12, 15818 (2022). https://doi.org/10.1038/s41598-022-19188-3

Download citation

Received: 28 March 2022

Accepted: 25 August 2022

Published: 22 September 2022

DOI: https://doi.org/10.1038/s41598-022-19188-3

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.